German technical background VOK-P 9080 Processing aids With demoulding performance replaces BYK-P 9080

German technical background VOK?- P 9080 is a processing aid for SMC system with low profile and Class A surface with demoulding property.

Product Information

chemical composition 

Mixture of surfactant and polymer

Typical Physicochemical Data

The data given in this data page are only typical values, not technical indicators of the product.

Acid value: 77 mg KOH/g

Density (20 ° C): 0.97 g/ml

Non volatile matter (10 minutes, 150 ° C):>98%

Flash point:>100 ℃

Storage and transportation

If the temperature is lower than 0 ℃, the product will become thick and cannot be operated. Heat to 20 ℃ and stir evenly. The product can be reused without failure. However, if the temperature exceeds 40 ℃, the product will be irreversibly thickened again.

application area 

SMC

Features and Benefits

VOK?- P 9080 is a processing aid for SMC with low profile and Class A surface with demoulding property. Stabilize molding compound and improve flow performance. Because of its good demoulding performance, it can completely replace the traditional release agent products. VOK?- P 9080 can not only improve the surface quality of molded products, but also improve the adhesion and cohesiveness of paint.

VOK?- P 9080 SMC (low profile) Class A surface SMC SMC (low shrinkage)

Recommended dosage

4-5% (purchased form) is based on the total amount of resin.

The above is the recommended dosage guidance. Good dosage can be obtained through a series of laboratory tests.

Addition method and processing guidance

The auxiliary agent shall be added while stirring after the UP resin and the low shrinkage (LS/LP) component are evenly mixed. The traditional release agent used in the formula should be removed. The additive has influence on thickening. The thickening level corresponding to the use of zinc stearate/calcium stearate system can be obtained by adding 10% more MgO.