EXCELLENT EPOXY PROTECTIVE ALLOY COATING PRIMER FOR STAINLESS STELL

PRODUCT NUMBER

No. 1020

TYPE

A two-pack, special alloy primer based on epoxy resin, hardener and special pigments.

USES

Used for galvanized steel, aluminum, alum-alloy metal and stainless steel after cleaning. 

CHARACTERISTICS

1.  Very fast drying with excellent adhesion.

2.  Very good adhesion with galvanized steel, aluminum, alum-alloy metal and stainless steel.

3. Very good resistance to weather and abrasion

4. Excellent resistance to weathering with very thin thickness (25μ).

FINISH

Flat

COLOR

Light Yellow-Green

SPECIFIC GRAVITY

Above 1.29 Kg/L (Mixture)

FLASH POINT

Above 20℃ (Mixture)

DRYING TIME(25℃)

Set-to-touch 2hr

Dry Hard 10hr

Fully Curing 7 days

OVERCOATING INTERVALS

Min. 8hrs.        

Max.  6 moths  (25℃)

OPTIMUM FILM THICKNESS

Wet 100 microns

Dry  50 microns

THEORETICAL COVERAGE

37.8 meter square/Gal

10.0 meter square /L

7.8 meter square /Kg

THINNER

SP-12 Epoxy Thinner

THINNING RATE

5 ~ 10 % (by wt., excluded cleaning tools) 

SUBSEQUENT COATS

Satisfactory with all coating system except  inorganic zinc primer.

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

APPLICATION METHOD

AirlessSpray,Brush

FOR AIRLESS SPRAY

Tip Size :  Graco  617/719

Air Pressure :  3~4 Kg/cm²

VISCOSITY  :  18~23sec.(Ford Cup No.4)

NOTE

1. Mix base and hardener according to the mixing ratio and stir thoroughly.

2. Avoid applying paint in rainy or humid weather particularly a wet surface must be thoroughly dried. 

3.All equipment must be cleaned immediately after use. 

4.Moisture, grease, sludge, old paint and rust must be thoroughly removed from substrate. 

5.The zinc white material formed in galvanized steel must be moved before application.