Ti Alloy Cp Grade 2 Triangle Tubes Cold Drawn Titanium Seamless Tubingtitanium Grade 5 Hollow Tubes Tubing Grade 5 Titanium Coil Tube

Titanium Pipe grade 2 bars have a density of 4.51 g/cm3, about 60% of the density of steel. This makes ASTM B348 UNS R50400 Pipe an ideal material for lightweight applications. It also has a melting point of 1660°C and a boiling point of 3260°C, which means it can withstand high temperatures. DIN 3.7035 Pipes has a shiny metallic appearance and is non-magnetic, which makes Alloy Pipe Grade 2  useful in certain electronic and medical applications.

• Density: 0.163 lbs/in3, 4.51 g/cm3

• Mean Coefficient of Thermal Expansion, in/inl° F (mm/ml° C):

• 70 - 212 ° F (20 - 100 ° C): 4.78 x 10-6 (8.6)

• Thermal Conductivity: BTU-in/h-ft-° F (W/m-° K):

• At 70 ° F (21 ° C): 114 (16.4)

• Modulus of Elasticity, ksi (MPa)

• 2 x 103 (105 x 103) in tension

• Melting Point: 3040 ° F (1670 ° C)

Ultimate Tensile Strength: 50 KSI min (345 MPa min)
Yield Strength (0.2% offset): 40 - 65 KSI (276 - 448 MPa )
Elongation: 20% min

#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.
#2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA - Bright annealed cold rolled and bright annealed
#CBA - Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled
#2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.
Polished - Various grit finish for specific polish finished requirements.

• Weldability - Fair

• Forging - Rough 982°C (1800°F), finish 968°C (1775°F)

• Annealing - 732°C (1350°F), 4hr, FC to 566°C (1050°F), A.C. F.C. not necessary for bars

• Solution Heat Treating - Forgings

• Aging - 904-954°C (1660-1750°F), 5 min-2hrs, W.Q. 538°C (1000°F), 4hr, A.C.