High Strength Monolithic Chrome Corundum Casting Refractory Castables

Chrome Corundum Casting Castables

Introduction:

Chrome Corundum Casting Castable (also called Chromium Corundum Refractory Castable or Chromium Corundum Castable), which is with chrome oxide and corundum as the main raw materials, through high pressure forming, high temperature firing and made of alumina and chrome oxide content is not less than 90%, chromium oxide content is not more than 50% of the shaped refractory products.

The main compositions of chrome corundum castable are AL₂O₃ and Cr₂O₃, these two components can form a continuous solid solution. adding Cr₂O₃ to the AL₂O₃ single-phase material not only increasing the thermal ability of the material in high temperature atmosphere, but also increasing refractoriness for the chromium and corundum combined castable. the melting point of this solid solution is at high temperature above 2050��C, which has high temperature resistance, washing and abrasion resistance. Cr₂O₃ can improve the slag corrosion resistance and spalling performance of refractory products. Therefore, the service life of chrome corundum castable is longer than normal corundum castable.

Properties

l  High abrasion resistant ability, corrosion resistance,

l  high refractoriness under load(1700�?/span>) and so on.

l  High compressive strength and high stability of the high temperature lining.

l  Large bulk density, overall lining resistance to slag erosion and strong permeability.

l  Anti-solid particles, dust, high-temperature gas flushing.

l  Small mechanical abrasion resistance.

l  Not affected by reducing gases such as H₂ and CO.

l  The construction is convenient. It can be cast into an integral lining, or it can be poured into prefabricated blocks or prefabricated parts.

Physical & Technical Index

Characteristics
(1) High temperature resistance and high operating temperature.
(2) Under 0.2mpa pressure, the softening temperature of the load is high.
(3) high temperature volume stability, high strength.
(4) Anti-slag slag has strong chemical corrosion.
(5) The construction is convenient. It can be cast into a seamless inner lining, or it can be prefabricated into cast precast blocks.
(6) The overall structure is stable and resistant to spalling.
(7) Quenching and rapid heat resistance, excellent thermal shock resistance.

(8) High-strength explosion-proof, to prevent the cracking or peeling of the surface of the cast lining due to baking.

Production Process of Chrome Corundum Castable

Chrome corundum Castable is made of ��- AL₂O₃ as raw material, adding appropriate amount of chromium oxide powder and chrome corundum clinker fine powder, forming and firing at high temperature. It can also be prepared by mud casting. ��- AL₂O₃ powder and chromium oxide powder are mixed evenly. Thickeners are made by adding glue and organic binders. At the same time, part of the chrome corundum clinker is added, and the castable is made by grouting method.

Applications:
It is widely used in kilns, furnaces and thermal equipment of metallurgy, petroleum industry, chemical industry, building material, machinery, etc.
Cr₂O₃ in chrome corundum castable has very low solubility in molten slag, as Cr₂O₃ can enhance the viscosity of molten slag, then the dissolution erosion rate of chrome corundum castable is reduced. So chrome corundum castable is important refractory material used for oxidizing atmosphere melting furnace working lining.  