Thomas high temperature resistant electronic components encapsulating adhesive

Outline

It is   double-component epoxy adhesive. It is easy and convenient to use for it   solidifies fast at normal temperature and bonds well. The surface of the   bonding is bright and smooth.

Applications

This product is   widely applied to the bonding of such materials as motor magnetic ring   (magnetic coil), magnetic metal, ceramics and composite materials in   especially the high-speed electric machines. It also applies to the bonding, sealing,   filling, repairing such materials as magnetic steel and magnet. 

Features

The A component   is dope with various colors, The B component is transparent liquid.

Fast curing   speed. At 25 °C, within 1-3 hour, the surface cures, and 2 days later, it reaches   its maximum bonding strength.

Being durable and   resistant to ultraviolet light, once the bond has formed.

Being   heat-resistant, it adapts to a wide range of temperature and bonds well under   high temperature.

Mix the two   components in a certain proportion, apply it to the surface of the substrates   directly, which makes it so convenient to use.

You.ll see long   term durability and resistance to moisture, chemicals, oils, and temperature   extremes.

Non-toxic after   solidification, though it is a little smelly.

Shelf life is one   and half a year.

The main   technical parameters are as follows:

Temp. resistance   scope：-52 °C－+225 °C

at room   temperature: Tensile strength≥35MPa; Shearing strength≥28MPa peeling   strength: 29KN/M

at 150°C    tensile strength 3-5 Mpa    volume resistance: (25°C)   1×1015Ω.cm      

surface   resistance 2.5×1015Ω.cm   

voltage   resistance 20-25kV/mm   hardness shore D 85   water   absorbing capacity  24h＜0.1%   Tg:200°C

Instruction

1. Clean the   surface of the material, make sure they have no dust or oil on them, wait   until they are dry.

2. Mix A and B in   a proportion of 3:1-1.2 to get perfect bonding result at fastest speed at 25   °C

3. Spread the   mixture on the substrates, put them together and apply some strength on them,   finally, let them dry for 2-4 hours.

Notes

1. Use another   can or container to blend A with B. The tools used to get A and B should be   different.

2. A and B should   be mixed well.

3. It is   necessary to keep it well ventilated and away from fire.

4. If it has   contact with skin, you should wash thoroughly with soap and water.

5. It can be   stored at well-ventilated places with low temperature, and keep them away   from fire.

6. Cover the lip   after using it.