thomas high strength structural adhesive

Outline

It is a high-gloss   two-component modified resin structural adhesive.it cures at room temperature   or when heated.It is resistant to temperature shocks and with good   resilience. The most distinguishing feature is that the adhesive remains   pliable and tough after the bonding formed.

Applications

It is applied to   the bonding of polystyrene, PVC, ABS, PET, Kevlar,silicone rubber,   polyurethane etc. It also used to bond ceramics and metals.

Features

Part A is sticky   liquid with light color. B is sticky and colorless liquid.

Curing time: at the   temperature of 25 degC, the maximum bonding strength is reached within two   and a half days; If it is heated at the temperature of 80 degC, the good   bonding strength will be reached within 8 hours.

Being weather and   heat-resistant, it adapts to a wide range of temperature and bonds well under   high temperature.

Mix the two   components in a certain proportion, apply it to the surface of the substrates   acquiring no strict treatment, which makes it so convenient to use.

You’ll get long   term durability and resistance to moisture, chemicals, oils, and temperature   extremes.

if long-term   exposed to the atmosphere, surface and the performance of its fundamental   unchanged

Being stable, its   storage time is one and half a year.

The main technical   parameters are as follows:

Heat resistance   scope：- 70°C－+ 220°C  

peel strength   ≥29kn/m  Shearing strength≥28.5MPa

Water Absorption 100℃，RH100% ，0.01%

(3000hours later)   tensile strength 35MPa, pressing strength 175MPa

Impact ductility   17KJ/m*m surface resistivity 2.5×1015Ω  volume resistivity 251×1015Ω.cm    voltage resistivity 20-25kV/mm

shearing   strength≥26.8MPa(25°C)   13.4MPa(200°C)    hardness D65

Instruction

1. Clean the   surface of the material, make sure they have no dust or oil on them, wait   until they are dry.

2. Mix A and B at a   proportion of 3:1-1.2, mix them well.

3. Apply the   mixture on the substrates evenly. Put them together together and apply some   strength.

Notes

1. temperature   influences the curing time, the higher the temperature is, the faster the   curing time will be. But heating temperature shouldn’t be higher than 110 deg   C.

2. Use another can   or container to blend A with B. The tools used to get A and B should be   different.

3 A and B should be   mixed well.

4 It is necessary   to keep it well ventilated and away from fire.

5 If it has contact   with skin, you should wash thoroughly with soap and water.

6 It can be stored   at well-ventilated places with low temperature, and keep them away from fire.  

7 Cover the lip   after using it.