Solvent Free Crystal Low Viscosity High Hardness Clear Casting Epoxy Resin For Solar Cell

Specifications:

????????????????????????????????? Resin??????????? Hardener
Colour???????????????????????????? Clear????????????? Clear
Viscosity (25°C mpa.s)??????????? 2500~3500????????? 40~100
Density (25°C g/cm3)????????????? 1.10~1.15????????? 1.05~1.10
Flash point (°C)???????????????????? >140????????????? >140
3: Blending Ratio (Weight Ratio): 100:50
4: Operation Time: Mixing volume 100g, 40~50mins on the temperature 25°C.
5: Recommend The Use Of Technology:
a) Pro-processor: clean the surface of contiguous, it is the best coating after to dispose with chemical modifiers to ensure the good adhesive force.
b) Preheat Substrate Material (50~60°C).
c) Cementing.
d) Vacuum deforming or Flame deforming.
e) Curing.
6: Curing Condition:
25°C 9~12Hours or
65°C 80min or
70°C 60min
7: Characteristic after Curing:
Surface resistance (25°C Ω ) 1.4×1015
Voltage proof (25°C Kv/mm) 16~18
Compression strength (Kg/mm2) 8.4
Distortion temperature (°C) 100
Water absorption rate (% . 24hr) < 0.1
Hardness (HD) 80~85

Description:

CW-D-201 is a solvent free crystal clear epoxy resin system, used for solar panel casting and coating, senior crafts transparent drape, electronic apparatus transparent, also can use as clear binder.
Product Features
Excellent UV resistance.
High hardness, with high anti-peel strength

Good process performance, low viscosity, low smell, quickly curing, curing on normal temperature or heating cure.
Transparently after curing, high surface brightness, smooth.