(SOLVENT-LESS) MADE IN TAIWAN EPOXY PAINTING OIL BASED EPOXY TRANSPARENT PAINT

(SOLVENTLESS) EPOXY FLOOR COATING

TYPE

A two-pack finish coating based on special solvent-less epoxy resin and hardener with chemicals resistance pigments.

USES

Anti-corrosive paint for chemical plants, power plants, steel factories.

CHARACTERISTICS

1. Tough and hard coat film with very good adhesion.

2. Brush one coat can obtain above 200 microns.

3. Excellent water and oil resistance

4. Excellent chemical resistance and anti corrosion.

5. Excellent mechanical wear resistance and electric insulation.

COLOR

Limited, please refer to color card

GLOSS

Above 85%

DENSITY

Above 1.35 Kg/L (mixture)

VISCOSITY

90 ~ 110 KU (25 ℃)

DRYING TIME

Set-to-touch 6 hrs. Dry hard 18 hrs. Full Dry 7 days (25 ℃).

OPTIMUM FILM THICKNESS

Wet 375 microns Dry 350 microns

MIXING RATIO

Base : Hardener = 15 : 4(by weight)

POT LIFE

30 minutes ( 25 ℃)

NON-VOLATILE CONTENT

Above 95% (mixture)

THINNER

Epoxy Thinner(cleaning tools only)

THINNER RATE

0

APPLICATION METHOD

Trowel and brush.

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

NOTE

1. Mix base and hardener according to mixing ratio and stir thoroughly then use

    completely in five minutes.

2. Adhered moisture, grease, dirt, rusts and corrosive salts on substrate must be

    cleaned thoroughly.

3. Avoid applying the paint in rainy weather or humidity above 85% RH,

    particularly a wet surface must be thoroughly dried.

4. All equipments must be cleaned immediately after use.

5. When directly apply on the surface of cement products, the surface must be

    completely dried.

6. When overcoating interval is exceeded, the paint film must be roughened to

    insure adhesion.