Injection molten iron samplers for foundry made in China

The main characteristics and applicable scope

For remove the steel sample,iron sample quickly  for spectral analysis,it's characteristics is simple structure and convenient application

 Usage

1. Insert the sampler for measuring gun;

2. When measuring the inserted steel (iron) water depth of 350 mm to 400 mm, molten steel sampling time 4 ~     6 s, molten iron sample time is 3 ~ 5 s;

3. The sampler from steel (iron) in the water, cooling, after moving lightly on the ground, the sample will fall to       the ground.

Type

1.According to whether the deoxidant is added in sampler,immersion molten steel sampler can be classified as deoxidant kind and without deoxidant kind.

 2.According to shape of sampler cup,immersion molten steel sampler can be classified as round sample, oval sample,dual thickness immerse sampler tips

Note

1. sampler moisture during storage must be prevented;

2. The steel temperature must be sampled at least 1400 ℃;

3. Avoid strong vibration, in order to prevent crushing the quartz tube;

4.KxQY-1 as having deoxidizer, high oxygen content of the molten steel is suitable for sampling; KxQY-2 is no oxygen scavenger, low oxygen content of the molten steel is suitable for sampling.

Technical Parameters

1.Sampling character: ≥95%

2.Steel sample:full,dense,smooth,without air hole

3.molten steel sampling time: 4 ~ 6 s