adhesive heat shrink mini cap

ProPerty

Test Method

Typical Data

Tensile strength

ASTM D 2671

10.4Mpa (min.)

Tensile strength after aging

158℃,168 hrs

ASTM D 2671

Remains 70%

Elongation at break

ASTM D 2671

200% (min.)

Elongation at break after aging  158℃,168 hrs

ASTM D 2671

100% (min.)

Longitudinal shrinkage

UL 224

0 to - 10%

Heat shock

250℃,4hrs

No cracking,no dropping

Cold bend -40℃,1hr

ASTM D 2671

No cracking

Voltage withstand

AC 2500V,60 seconds

ASTM D 2671

No breakdown

Volume resistance

ASTM D 876

10¹⁴Ω.cm (min.)

flammability

SAE-AMS-DTL-23053/5

Self extinguish in 30 sec.

Copper corrosion

158℃,168 hrs

UL 224

pass

Water absorption

ASTM D 570

< 0.5%

Part

Number

Standard

Length

as supplied

(mm)

Inner Diameter as supplied (Min)

Inner Diameter Recovered

(Max)

Recovered Total wall Thickness (Min)

Recovered Jacket wall Thickness (Min)

Recovered Adhesive wall Thickness (Min)

HSMC-E-1

30.35

5.72

(0.225)

1.27

(0.050)

1.20

(0.047)

0.64

(0.025)

0.56(0.022)

HSMC-E-2

30.35

7.44

(0.293)

1.65

(0.065)

1.52

(0.060)

0.76

(0.030)

0.76(0.030)

HSMC-E-3

40.50

10.85

(0.427)

2.41

(0.095)

1.91

(0.075)

0.89

(0.035)

1.37(0.054)

Part

Number 

Size

Total Length as supplied

Workable Length as supplied

Inner Diameter as supplied (Min)

Inner Diameter recovered (Max)

Recovered Total Wall Thickness

HSMC-D-1

1/8

22.0

(0.87)

12.7

(0.50)

3.2

(0.125)

0.58(0.023)

1.22±0.15(0.048±0.006)

HSMC-D-2

3/16

25.4

(1.00)

15.2

(0.60)

4.8

(0.187)

1.52(0.060)

1.57±0.20(0.062±0.008)

HSMC-D-3

1/4

28.4

(1.12)

15.2

(0.60)

6.4

(0.250)

2.03(0.080)

1.98±0.20(0.078±0.008)

HSMC-D-4

3/8

31.8

(1.25)

18.3

(0.72)

9.5

(0.375)

2.29(0.090)

2.08±0.25(0.082±0.010)

HSMC-D-5

1/2

38.1

(1.50)

21.6

(0.85)

12.7(0.500)

2.29(0.090)

2.54±0.25(0.100±0.010)