5083 Industrial aluminum sheets 5052 environmental protection equipment mechanical processing aluminum alloy sheets laser cutting 3003 aluminum sheet

?Size: Thickness: 0.15-600mm  

?, width, width: 20-2650mm  

? Service features: Original warranty, 7-45 days delivery, global export  

? Application: Ship plate, LNG storage tank, gas storage tank, GIS shell, body skin, flange material, etc  

Product introduction  

5083 aluminum plate is the star product of Juye Aluminum, juye Aluminum 5083 aluminum plate, the widest up to 2650mm.  Juye aluminum strictly controls the product process of 5083 aluminum plate. Through the determination of alloy composition, optimization of casting process, homogenization heat treatment and rolling process test, the product performance is comparable to that of foreign materials, which meets the increasing processing demand of Marine aluminum plate, rail transit, automobile, mold and other complex parts, and has a very broad application prospect.  

5083 aluminum plate performance advantages:  

1, high strength, good fatigue performance  

2. Good corrosion resistance of Marine atmosphere  

Good weldability  

5083 aluminum plate (high magnesium Marine aluminum alloy plate) is a typical weldable aluminum magnesium alloy plate with high strength and corrosion resistance, which is a necessary raw material for hull manufacturing. However, the hull of contemporary ships is complicated and curved, and the production process has high special requirements. How to produce and process a better hull shape?  Into the more 5083 aluminum plate manufacturers more aluminum plate manufacturers must treat the big problem, Ji 'nan Juye aluminum for you to tell you about the technical process:  

In the hull welding forming, involving hull complex surface, 5083 aluminum plate outer plate forming production processing, mentioned the magnetic field force assisted aluminum alloy plate line heating forming production process.  The whole process of fabrication and test of magnetic field force assisted wire heating forming of aluminum alloy plate is introduced, and the actual effect of magnetic field force assisted forming is proved by full use of original data.  Involving the supply of 5083 aluminum alloy plate, 5083 aluminum alloy plate magnetic force auxiliary line heating forming process, using ANSYS software for three-dimensional numerical simulation, the influence of magnetic force auxiliary function time and pulse current amplitude on the actual effect of magnetic force assisted forming;  On this basis, the forming mechanism of 5083 aluminum alloy plate in the whole process of magnetic field-assisted wire heating molding was studied from the perspective of the periodicity of pulse magnetic field force and the cyclic loading and unloading of the load generated by the magnetic field force.  

5083 Aluminum plate chemical composition:  

Aluminum Al: allowance  

Si Si: 0.4 or less  

Copper Cu: 0.1 or less  

Magnesium Mg: 4.0-4.9  

Zinc and zinc: 0.25  

Manganese Mn: 0.40-1.0  

Ti Ti: 0.15 or less  

Chromium Cr: 0.05-0.25  

Iron Fe: 0.4  

Individual: 0.05  

Total: 0.15  

Mechanical properties of 5083 aluminum plate:  

Tensile strength σ B (MPa) : 110-136  

Elongation δ10 (%) : ≥20  

Annealing temperature: 415℃.  

Yield strength σ S (MPa) ≥110  

Sample blank dimensions all wall thicknesses  

Elongation of 5083 aluminum plate δ5 (%) ≥12