ASTM 1.2510, 100MnCrW4, O1 tool steel round bar

ASTM 1.2510, 100MnCrW4, O1 tool steel round bar packed with waterproof paper or weave bag, into pallets or wooden case.

ASTM 1.2510, 100MnCrW4, O1 tool steel round bar 

Comparable Standards:                                                                                                                                    

 Chemical Analysis (%):                                                                                                                                    

Heat treatment                                                                                                                                                   

Hardening:

-   Temperature: 780-830°C(Slow heating and pre-heat at 350°Cand 650°C).

-   Duration: 30 mins per 25mm thick.

Quenching:

-   Medium: warn oil, salt bath.

Double Tempering

-   Temperature (2 hrs minimum) 250°C, better toughness.(58-59HRC).

-   Temperature (2 hrs minimum) 200°C, higher hardness. (60-61HRC).

 Size Available

 1) Round bar: Dia 50mm-500mm  2) Flat bar: Thickness: 16-500mm Width: 200-1000mm Length can be customized. 

Smelting Process EAF+LF+VD 2) EAF+LF+VD+ESR

Shaping Hot forged / Hot rolled

Surface condition: Black surface/turning/milling/grinding/polishing

Annealing Hardness: HB229 Max 

Properties: Under medium temperature conditions, it has good toughness, thermal strength, thermal fatigue and wear resistance. Less thermal deformation and less oxide skin when air quenching, erosion against molten aluminum.  

Application: Widely used in making casting die, thermal extruding die for machining aluminum casting parts, tools for punching holes, core rod

Weight(kg): Round bar=0.00617*R*R*L   Flat bar=0.00785*T*W*L

Characteristic

1)Better toughness than conventional H13  2)Fine grain size with high toughness  3)High Strength at elevated temperature.