Incoloy 925 round bars bolts and nuts fasteners

High Performance Incoloy 925 / UNS N09925 Nickel Alloy Round Bar ASTM B805:
Delivery Time:25-30 days
Certification:CE,FCC,MSDS
Incoloy 925 / UNS N09925 Nickel Alloy Round Bar ASTM B805
1. Grade: Incoloy 925
2. Process: VIR - VAR - ESR - Forging - Semifinished - Finished
3. Delivery Condition: Forged, Solution Annealed, Aged
4. Surface Condition: Black, Machining
5. OD: 6-500mm
6. Specification: ASTM, ASME, GB, JIS, GOST, DIN, etc.
7. Packing: Plywood case, Bundle

General Characteristics of Incoloy 925
Incoloy 925 is a precipitation-hardenable nickel-iron-chromium alloy. It combines high strength with Incoloy 825's excellent corrosion resistance. Incoloy 925 is particularly resistant to sulfide-induced stress cracking and stress-corrosion cracking.

Chemical Composition of Incoloy 925

Physical properties

Heat Treatment of Incoloy 925
Anneal by holding at 1800°F (982°C) for ? to 1 hour, then rapidly cool (air cool small sections, water quench others) Aging Heat to 1400°F (760°C) Hold at temperature 8 hours Furnace cool at 100°F (38°C) per hour Hold at 1150°F (621°C) for 8 hours Air cool
Applications of Incoloy 925
Oil industry, including tool joints, tubular products, and parts for intermediate sour-gas wells Fasteners Pump and marine shafting Strong, seamless piping and tubing
Machinability of Incoloy 925
Perform on hot-worked metal suggested to provide best finish while conserving machining
Workability of Incoloy 925
Hot working Similar to Incoloy 825 up to 2000°F (1093°C) - higher temperatures produce a stronger, less-ductile metal 1600° to 2150°F (871°  to 1177°C) hot working range Perform final hot working from 1600° to 1800°F (871° to 982°C) for top mechanical properties and best corrosion resistance Cold working Higher work-hardening rate than Incoloy 825