Ultrafine Portland cement grouting performance

BiaoYUAN Micro Fine Cement is mainly composed of CaO, SiO2,Al2O3, Fe2O3 and so on. Other ingredients such as ignition loss, SO3, MgO, insoluble substance and so on should meet the requirements of GB175 and BS EN 197.

Introduction:

BiaoYuan microfine cements are blast furnace slag based cements composed of ultrafine particles and are designed for injection into loose soils, rock and concrete. They feature a maximum grain size ranging from a d95 of 6μm to a d95 of 16μm. Depending on the application and the permeability of the strata, different grain size can be used. It is suited for stabilizing or sealing all earthen foundations; especially for permanent structures such as tunnels, dams, deep foundations and oil storage tanks. Because they cure into a hardened concrete, BiaoYuan microfine cements cause no pollution to underground soils or water supplies. 

Feature:

-excellent penetration in tight joints, fissures and pore spaces 

-improved water tightness following proper application 

-better working environment 

-improved grouting efficiency and less waste 

Technical Date:

product unit dmfc-600 dmfc -800 dmfc -1200 

appearance grey powder grey powder grey powder 

odor none none none 

toxic none none none 

specific gravity kgdm3 ～3 ～3 ～3 

specific surface area m2kg ≧600 ≧800 ≧1200 

grain size d50 μm ＜6.75 ＜4.38 ＜3.21 

grain size d90 μm ＜16.31 ＜9.68 ＜7.55 

grain size d95 μm ＜22.97 ＜12.86 ＜10.51 

setting times

(measured by vicat needle) initial set min 60 120 60-120 

final set min 120 150 120-150 

compressive strength 3 d mpa 25 25 25 

7 d mpa 45 45 45 

28 d mpa 60 60 60