Casing Pipe P110-28Cr

API 5CT P110 28Cr Casing Pipe Threaded with Couplings

Specifications:Casing Pipe P11028Cr API H40Minimum 

Yield Strength: 40,000 psiMaximum 

Yield Strength: 80,000 psiMinimum 

Tensile Strength: 60,000 psi

Notes: General purpose pipe manufactured to API specification 5CT.

API J55Minimum Yield Strength: 55,000 psiMaximum 

Yield Strength: 80,000 psiMinimum 

Tensile Strength: 75,000 psi

Hardness Requirement: NoneNotes: General purpose pipe manufactured to API specification 5CT. 

Similar to K55 except the minimum tensile strength is lower. Usually, 

this grade is used in tubing applications.

API K55Minimum Yield Strength: 55,000 psi

Maximum Yield Strength: 80,000 psi

Minimum Tensile Strength: 95,000 psi

Hardness Requirement: NoneNotes: General purpose pipe manufactured to API specification 5CT. 

Usually, this grade is used in casing applicationsAPI L80

Minimum Yield Strength: 80,000 psiMaximum 

Yield Strength: 95,000 psiMinimum Tensile Strength: 95,000 psi

Hardness Requirement: 23 HRC maximum

Notes: Manufactured to API specification 5CT. 

This is a controlled yield strength material with a hardness testing requirement. 

L80 is usually used in wells with sour (H2S) environments.

API N80 (or N80 Q&T)Minimum Yield Strength: 80,000 psi

Maximum Yield Strength: 110,000 psi

Minimum Tensile Strength: 100,000 psi

Hardness Requirement: None

Notes: General purpose pipe manufactured to API specification 5CT.

API Normalized N80Minimum Yield Strength: 80,000 psi

Maximum Yield Strength: 110,000 psi

Minimum Tensile Strength: 100,000 psi

Hardness Requirement: None

Notes: A lower-cost alternative to standard Quench and 

Tempered API N80 (walls less than 0.500 inch). Inspection, 

testing and dimensions are in accordance with API 5CT for grade N80. 

Charpy v-notch impact test absorbed energy results meet API SR16 and 

are lower than Quench and Tempered N80.API C90

Minimum Yield Strength: 90,000 psi

Maximum Yield Strength: 105,000 psi

Minimum Tensile Strength: 100,000 psi

Hardness Requirement: 25.4 HRC maximum

Hardness testing is conducted as required for API T95, 

with the exception of frequency (Casing and Non-Upset Tubing - First, 

last and every tenth joint in between; Upset Tubing - First, 

last and every 25th joint in between). To reduce order lead time, 

sulphide stress corrosion cracking (SSCC) testing is not required for every order.

If required by the customer, SSCC testing can be performed to U. S. 

Steel Standard Mill Practice P-1004 (NACE Standard TM-0177-Method A) with 

a guaranteed minimum threshold stress of 85 percent specified minimum yield 

strength.API T95Minimum Yield Strength: 95,000 psi

Maximum Yield Strength: 110,000 psi

Minimum Tensile Strength: 105,000 psi

Hardness Requirement: 25.4 HRC maximumNotes: API controlled 

yield strength grade, the same as API C95. 

Generally for use in sour condensate wells.

 Extensive hardness testing is required along with SSCC testing per NACE 

Standard TM-0177Method A. 

The minimum threshold stress required is 80 percent of specified 

minimum yield strength.API P110

Minimum Yield Strength: 110,000 psi

Maximum Yield Strength: 140,000 psi

Minimum Tensile Strength: 125,000 psi

Hardness Requirement: NoneNotes: API grade for general use in deep wells. 

This grade is not generally considered suitable for sour condensate wells.

API Q125Minimum Yield Strength: 125,000 psi

Maximum Yield Strength: 150,000 psi

Minimum Tensile Strength: 135,000 psi

Hardness Requirement: No limit specified - Hardness variation requirement

Notes: API grade for deep well service, not generally for use in sour condensate wells.

Quadrant hardness testing is required without any specified limits other than the variation between readings. Impact testing is required for each heat and/or lot. NDT inspection is required with two methods of inspection (typically EMI and UT are performed on this product).V150Minimum Yield Strength: 150,000 psiMaximum Yield Strength: 180,000 psiMinimum Tensile Strength: 160,000 psiHardness Requirement: NoneSteel grade for use in deep well applications. Dimensions and inspection are in accordance with API 5CT Group 3 requirements.Standards:API Specification 5CT latest edition at time of manufacture (PSL-1, PSL-2, PSL, 3)ISO 11960:2011-06 (E). Petroleum and natural gas industries - Steel pipes for use as casing or tubing for wells.ISO 13680-2010 Petroleum and natural gas industries-Corrosion-resistant alloy seamless 

tubes for use as casing,tubing and coupling stock-Technical delivery conditions

ISO/TR 10400:2007 Petroleum and natural gas industries -- Equations and calcula

tions for the properties of casing, tubing, drill pipe and line pipe used as casing 

or tubingGOST 632:1980 Casing pipes and couplings.GOST 633-80 pumping and

 compression pipes-D, K, E, LNORSOK M-703-CR Casing and tubing materials 

(Rev[1]. 1, Jan. 1996)DEP 39.01.20.10-Gen L80 13%Cr casing and tubing

 (amendments/supplements to ISO/DIS 11960.2)DEP 39.01.20.30-Gen 

Corrosion-resistant alloy seamless tubes for use as casing, tubing and coupling 

stock - technical delivery conditions (endorsement of ISO 13680)

DEP 39.01.20.31-Gen Care and use of casing and tubing (endorsement of 

ISO 10405)GOST 632-80 Specification of Casing Pipe and Couplings form 

THEMPDVSA EM-18-00-05 Requirements for Casing and TubingOCTG

 (Casing & Tubing)?API 5CT Latest Edition?OCTG from 1.660" to 30'' + respective

 couplings, crossovers and pup joints?API Grades from H40 to Q125 and 

13% CR?ALL API Standard Weights?API and Premium Joint Connections?Special 

SS and HC grades?CRA GradesSection: Seamless & WeldedSizes:Outside 

Diameter: 1.660" - 30"Grades:H40, J55, K55, N80-1,N80-Q, L80-1, C90-1,C90-2, 

C95, T95-1,T95-2,T95-3, P110, Q125-1, Q125-2,Q125-3,Q125-4.13Cr 

Series:L80-13Cr,C95-SP13Cr1,C95-SP13Cr2,P110-SP13Cr1,P110-SP13Cr2

Connections:?STC (short round thread casing)?LTC (long round thread casing)?

BTC (buttress thread casing)?XL (extreme-line casing)?NUE (non-upset tubing)?

EUE (external upset tubing)?IJ (integral joint tubing)?Premium 

ConnectionsAnd almost any premium & gas tight connection

Length:Range 1, Range 2 & Range 3:

Applicable Tests:See our Standard Inspection ScopeProtection:External bare 

and uncoated or externally coated with black/ transparent anti rust Mill 

varnishPlastic or Metal Pin and Box Protectors.Internal plastic coating or 

sleeves.Mill Test Certificates:Issued in accordance with API Specification 5CT 

Eighth EditionAdditional Third Party Inspection can also be performed on 

request.A wide range of Casings and Tubing are available from Stock:

DIMENSIONAL & WEIGHT TOLERANCESOutside Diameter (OD) up to 4" +.031",

 -.031"4 1/2"+ +1%, -0.5%, not to exceed .125"Wall Thickness +0, -12.5%Weight

 single joint +6.5%, -3.5%carload (>40,000#) +0, -1.75%Drift diameter up to 

2 7/8" OD (42" mandrel) d-3/32"3 1/2" to 8 5/8" (6" mandrel) d-1/8"9 5/8" to 

13 3/8" (12" mandrel) d-5/32"Straightness 4 1/2"+ 0.2% end-to-end (PE), 

.125" in 5' at each endLength Range 1 casing 16-25'Range 2 casing 25-34'

Range 3 casing 34-48'Range 1 tubing 20-24'Range 2 tubing 28-32'pup joints 

(2,4,6,8,10 &12') +3", -3"INSPECTION CLASSIFICATIONSNew

 Tubing/Casing(and Plain End Drill Pipe)*White Band: suitable for all inspections 

performed (incl. min. 87.5% body wall).*Yellow Band: Repairable reject. 87.5% 

body wall remaining after repair. Locate bands on either side and circle around 

defect.*Blue Band: Imperfections of undetermined depth. Identified as 

above.*Red Band: Defective length. Identified as above. Body wall defects must 

be cut out of tube.Damaged pin or box ends marked with red bands next to pin

 or on couplingDrift restrictions indicated by red bands on either side of 

restriction - just like other defects.Tube classification bands appear in same

 location (box end) as on used material.