Phenolic Cotton Cloth Laminated Sheets, Jointing Sheet / Rod

sizes: 1020 X 2040 mm.

Color: Dark Brown
Surfaces: Shining

Material: cotton cloth and phenolic resin

Phenolic Cotton Cloth Laminated Sheets, Jointing Sheet / Rod

Description:

Phenolic cotton cloth laminated sheet / rod

Properties: Excellent mechanical properties, high resistance to blows and vibrations, high resistance to friction, for general industrial applications.
Applications: Mechanized pieces of big size for mechanical applications such as ball bearing, silent gearing for modules superior to 2.5, ball bearing caps, pulleys. It also can be used as insulating construction parts in electrical equipment.
?this product is a stratified insulator made from cotton cloth and phenolic resin.
At delivery time the presentation of the sheets is as follows:

- Maximum sizes: 1020 X 2040 mm.
- Thickness: From 0.50 mm
- Colour: Dark Brown
- Surfaces: Shining
- On demand we can deliver strips or finished components.

PROPERTIES
- Excellent mechanical properties
- High resistance to friction
--Low hygrometric degree
- High resistance to splitting

Products range:
PVC fiberglass sleeving (vg-201)
Silicone fiberglass sleeving (srg)
Acrylic fiberglass sleeving (AG)
Silicone rubber fiberglass sleeving (frs)
Rubber inside/outer-fiberglass sleeving
Polyurethane fiberglass sleeving
Pure silicone rubber tube
Fire sleeving
Htg fiberglass sleeving
Fish paper, per-compressed paper board
6520 fish paper/polyster film composited foil
Dmd-b, dmd-f, dmdm
Nmn --- 6640
Mylar film, milinnex film
Polyimide film
Fiberglass tape
Cotton tape
Heat shrinkable tape
Silicone rubber adhesive tape
2210, 2310, 2432, 2450 varnish coated cloth/tape
Epoxy phenolic glass cloth laminated sheet
3416 --- phenolic cotton cloth laminated sheet
3417---- phenolic paper laminated sheet
3418 ----phenolic cotton cloth laminated rod
3419 epoxy phenolic glass cloth laminated rod.

Applications

Mechanized pieces of big size for mechanical applications such as ball bearing, silent gearing for modules superior to 2.5, ball bearing caps, pulleys. It also can be used as insulating construction parts in electrical equipment.
?

Specification

Density: 1.25 g/cm3
Bending strength: 117.6mpa (min)
Tensile strength: 78.4 mpa (min)
Breakdown strength(min): 10.0 kv (parallel to lamination at 20c in oil)
Insulation resistivity(min): 1x10e8 ω (perpendicular to lamination)
Water absorption (max): 1.0 %(1.0 mm)