Newest Restore titanium rotary kiln manufacturer with ISO

Specifications

Restore titanium rotary kiln process:
Ilmenite and reducing agents, desulfurizer preparate into raw materials, add into the rotary kiln, in a reducing atmosphere, heated to 1050 ~ 1180 °C for reduction, the reducing atmospheric pressure was maintained at 0 ~ 4mm water column, cooling, screening, magnetic election, impact winnowing, blending derived reductant and ilmenite feedstock weight ratio is 0.3 to 0.6:1,

desulfurization agent and reducing agent weight ratio is 0.02 to 0.2:1.

The method achieve continuous flow operations, greatly improving production efficiency and shorten reaction time reduction, and easy to control the temperature uniformity, thus ensuring product quality to meet the needs of production welding. Rotary kiln system with fire clay refractory lining masonry, the mortar joint should be less than 2mm, the construction should be strictly controlled. Fixed fire equipment lining gray mud cracks should be full, and the upper and lower inner and outer layers of brick joints should be staggered. Masonry should be sought Zhuanfeng straight or curved smooth, dense masonry. For kiln refractory lining tube must also ensure that brick kiln ring with concentric cylinder reliably, it should ensure that the tile kiln shell completely tie with tight, brick and inter-face contact should be firmly bonded. Masonry brick lining does not move the device when the fire mud plumpness required to achieve 95% or more, use the puree pointing surface cracks between the blocks, but the extra time scraping mud brick lining surface.

Restore titanium rotary kiln technical parameters:

 Note: table parameters only for type selection reference.