YG8 USD160 PER PCS tungsten carbide disc cutter/PCS BLADES,LEAD WIRE CUTTERS

Grade

Performance

Performance&application recommended

Density

Bend Strength

Hardness

G/Cm3

N/mm2

HRA

YG6A

14.95

1800

92.5

Fine grain alloy, good wear resistance,Semi-finishin of chilled

cast iron, non-ferrous metals alloys, semi-finishing and finishing

of hardened steel,alloy steel.

YG8

14.8

2200

89.5

High strength in use,impact and shock resistnace higher than

YG6,but wear resistance and cutting speed comparatively lower

Roughing of cast irons, non-ferrous metalsand their alloys as

well as non metallic materials at low cutting speed.

YG10X

14.5

2400

91.5

Fine grain alloy, good wear resistance,Used for processing hard 

wood, veneer board,PCB,PVC and metals.

YL10.2

14.5

2400

91.8

Fine grade alloy,with high wear resistance,high bending strength

high resistance to bonding ,high termal strength,Machining of 

refractory alloys,stainless steel and high manganese steel,etc.

YG20

14.3

2420

90

Conventional wear resistance, high bending strength,used for 

steel alloy etc.

Properties and applications of tungsten carbide for disc Cutters

Grade

Performance & application recommended

Density

T.R.S

Hardness

g/cm3

MPα

HRA

SH6A

14.9

1850

92.0

ine grain alloy, good wear resistance. 

SH10A

14.8

2450

90.5

High wear resistance, high bending strength,,used for dis saw blads in electrical line.

SH25

14.8

2200

89.5

High strength in use, impact and shock resistance higher than YG6, but wear resistance and cutting speed comparatively lower. 

SH30

14.7

2320

89.5

Roughing of cast irons, non-ferrors metals and their alloys as well as non metallic materials at low cutting speed.

SH35

14.5

2200

91.0

Fine grain alloy, good wear resistance. Used for processing hard wood,veneer board,PCB,PVC and metals.

SH40

14.5

2480

92.0

Machining of refractory alloys, stainless steel and high manganese steel, etc.

SH50

14.3

2420

90.0

Conventional wear resistance, high bending strength,used for steel alloy etc.