Specifications

Free sample! 316l stainless steel sheet manufacturer,China

STAINLESS STEEL CONSERVATION

1. Clean frequently with a cleaner and water. Any cleaner that is safe for glass is usually safe for stainless steel.

2. Scrub off all rust from these objects with a scrubbing pad or steel wood pad. This means getting rid of rust from pots and pans before putting them into a stainless steel sink or on top of a stainless steel stove.

3. Put a rubber mat at the bottom of the stainless steel sink before placing rusted pots and pans (such as cast iron cookware) in the sink.

4. Apply a thin layer of lubricant (such as mineral oil) to the surface of the stainless steel. This prevents rust from forming.

316l stainless steel sheet

Instruction:

stainless steel plate /sheet AISI  316l

Stainles steel is a production which not easy rust,acid resistance and corrosion resistance,so it is widely

used in light industry,heavy industry,daily necessities and the decoration industry.my company long-term

supply stainless steel porducts including:stainless steel sheet,stainless steel coil and stainless steel tube

Chemical composition(WT%) 

(C):≤0.15 (Si):≤0.75 (Mn):5.5~7.50 (Cr):16.0~18.0 (N):≤0.25 (Ni):3.0~5.0 (P):≤0.060 (S) :≤0.030 

physical property

strength of extension:100,000 to 180,000 psi; 

yield strength:50,000 to 150,000 psi;

elongation :55 to 60% 

modulus of elasticity:29,000,000 psi; 

density :.280lbs/cubic inch(7.93g/cm3)

Hot rolled steel plates are appropriate for construction works, oil & rig industry, pipe Industry, machinery industry, ship building Industry and other downstream industries. Moreover we also provide sales executives and engineer team for giving the products information to the customers.

Machinability

Stainless steel 316l has good machinability. Machining can be enhanced by using the following rules:

• Cutting edges must be kept sharp. Dull edges cause excess work hardening.
• Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.
• Chip breakers should be employed to assist in ensuring swarf remains clear of the work
• Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.