Autoclaved Aerated Concrete Block Plant

Specifications

                              Autoclaved Aerated Concrete Block Plant

    * Advantage of AAC Block Plant:

1.Light-weight :

The AAC block weight usually is 500-700kg/m3. It apply to fill walls of high-rise building and the main wall of low-rise buildings to make the whole building self-weight than normal weight reduce above 40% of composite masonry structure building . And that improves much building anti-aseismic ability. 

2.Good heat preservation:

The AAC block coefficient of thermal conductivity is commonly 0.11 0.18 kcal/m 0  hour.

The heat preservation effect of 20 cm aerated concrete wall is equivalent to 49 cm thick clay brick wall thermal insulation effect. Obviously the heat insulation performance is significantly superior to 24 cm brick wall. 

Thus,it greatly thin the thickness of wall body. Correspondingly it will expand the effective use of the building area, save construction materials thickness, improve the construction efficiency, reduce the engineering cost and weight of the building.

3.High strength: 

By experiment, aerated concrete block compressive strength is greater than 25 kg/cm2, equivalent to 125 clay brick and lime-sand brick compressive strength .

4.Nice anti-seismic performance:

The aerate concrete block is light-weight,good overall performance,small inertia force during the earthquake . 

5.High temperature resistance:

When temperature is below 600, the aerated concrete block compressive strength increased slightly, when the temperature is controlled in 600, its compressive strength is close to room temperature compressive strength, so the aerated concrete as building material fireproof performance meet national fire protection standards. 

Aerated Autoclaved Concrete plant, AAC block plant,aac  line,aac plant,AAC brick plant

1 )       Product weight is according to 600kg/m3 to control.

2 )      annual capacity 50,000m3-450,000m3

3 )       water and material rate 0.631

4 )       one mould product 2.88M3

5 )       Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.

6)       casting slurry temperature 38-42 degree

7 )       body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa

8 )       Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.

9)Cement lime Sand style aerated block raw material proportion

Cement lime fly ash style aerated block raw material proportion

 9). 

Summary:

Aerated concrete brick (light brick ) is the light and porous building material. It has light keeping temperature cant burn and other advantages.it can be made into many kinds of brick.they could be used in industry building and common building.they are more and more popular in the world.in the future,they will replace the Clay brick completely.