AAC Block Equipment 100000m3/year-Teng Fei Aac Block for Sale

Specifications

AAC block equipment 100000m3/year-Teng Fei aac block for sale

1. Basic Introduction of AAC block equipment 100000m3/year 

Autoclaved Aerated Concrete (AAC) is a siliceous material (sand, fly ash and silicon tailings such as waste porcelain clay, stone processing waste materials, blast furnace slag, etc.) and calcareous materials (lime, cement) as the main raw material, mixing fat gas agent (aluminum powder), by ingredients, mixing, casting, preraising, cutting, autoclave, curing process made of light porous silicate products, because by the hair contains a lot of gas even after the small pores, hence the name of aerated concrete.aerated autoclaved concrete plant, AAC block, aac production line, aac plant, AAC brick, autoclave aerated concrete block, concrete block machine, light weight block.

2. Advantages of  AAC block equipment 100000m3/year  

2.1, Lightweight:The aerated concrete dry bulk density generally is 400-800kg/m3, equivalently to clay brick 1/3, normal concrete 1/5, lower than normal light-weight aggregate concrete and hollow

 brick, hollow clay brick. so, using aerated concrete as wall material can lighten the building self weight, and then reduce the size of building foundation, girder and pillar etc. Structure, save building material and project cost, improve the building shock resistance.

Several common building material volume density (kg/m³)

2.2, Fireproof: Most of the major raw materials is inorganic materials, so it has good fire resistance, and do not emit harmful gases when meet fire. Fire 650 degrees, as a refractory material, the thick up of 90mm walls can reach to 245 minutes fire resistance, 300mm thick up wall can reach to 520 minutes fire resistance.

2.3,Sound insulation: Due to a unique porous structure, so it has a sound absorption capacity. The sound absorption capacity can reach of 10mm thick wall up to 41 db.

2.4, Insulation: As the material inside has a large numbers of the pores and porous, which has a good thermal insulation properties. The Thermal conductivity is 0.11-0.16W/MK, as 1/4-1/5 of brick. Typically, the insulation effect of 20cm thick aerated concrete wall is equivalent to 49cm thick solid brick walls ordinary.

2. 5, Permeability: Result of material by the composition of many independent small pores, the moisture absorption is slow, in the volume of absorbent is 5 times of clay saturation do. When used in the bathroom, the wall can be treated to interface directly paste tiles.

2.6, Anti-seismic:The same building structure, improve the two seismic than the brick level.

3. Performance of AAC block equipment 100000m3/year

Finished AAC block is Suitable for all nonbearing wall and bearing wall of multi-story (less than six-floor), nonbearing wall internal parting wall, thermal insulation rooms front panel, floorslab.

3.1, Unit weight grade (kg/m3): 500, 600, 700, 800 (means 05,06,07,08 grade)

3.2, Compression strength grade (Mpa): A3.5, A5.0, A7.5, A10.0 (1Mpa=10kg/m2)

3.3, Drying shrinkage (mm/m): =<0.8

 4. Normal size of AAC blockequipment100000m3/year  

   Length (mm): 600

   Width (mm): 75, 100, 125, 150, 175, 200, 250 

                              60, 120, 180, 240

   Height (mm): 200, 240, 250, 300

   Remarks: the size can be customized

5. Main Raw maerial of AAC block: AAC block equipment 100000m3/year

5.1 Typical Formula and Consumption of Fly ash AAC

Fly ash: content ratio 70%, consumption 350kg/m3;   Cement: content ratio 13.8%, consumption 25-30kg/m3;   Lime: content ratio 13.8%, consumption 140-150kg/m3;   Phosphogypsum: content ratio 2.96%, consumption 15kg/m3;   Aluminum: micro scale, consumption 0.4kg/m3

5.2 Typical Formula and Consumption of Sand AAC

Sand: content ratio 69.2%, consumption 350kg/m3;   Cement: content ratio 13.8%, consumption 70kg/m3;   Lime: content ratio 13.8%, consumption 70kg/m3;   Gypsum: content ratio 2.96%, consumption 15kg/m3;   Aluminum: micro scale, consumption 0.4kg/m3

6.2. After distributing,feed raw material into pouring mixer to make slurry

6.3. Through thoroughly mixing,the slurry is poured to mould

6.4. After pre-curing under a certain temperture and time,the block would reach a  certain hardness prepare for cutting

6.5. Tilting hoister would turn over 90 degree of mould

6.6. Then open the mould and separate it from block,and take the block woth side plate ti cutting cart

6.7. The blocks then be cut through the cutter firstly of two vertical sides of block

6.8. Secondly the horizontal cutting

7. Main equipments in AAC block equipment 100000m3/year

7.1, Material-milling Equipments:

a. Crusher: Lime, gypsum, and such kind of bulk material need to be crushed as the first step in AAC Plant.   

b. Ball mill: The AAC material must be fully grinded in order to make better reaction. Ball Mill is used widely, it has two types: dry and wet, can be chosen upon requirement.

7.2, Material Metering Equipments: Computer Control Automatic Metering System is commonly used as measurement of raw materials.

7.3, Material mixing and casting equipments: Mixer, it’s the slurry mixing machine, also is slurry casting machine.

 About us

1.Delivery time: 15 days after receipt of your deposit.

2.Payment terms: 30% T/T in advance, the left is paid (by T/T) before delivery.

3.Package:

1).Wire cables are used for fastening the machine on the trailer or inside the container.