Garden kneeling pad/EVA foam pad

Item No.

L-2500

C-1600

C-3000

H-25

H-35

A-25

Density
(g/cm^3)

0.021~0.027

0.035~0.041

0.023~0.029

0.065~0.075

0.07~0.08

0.08~0.09

Hardness
(type C)

15~21

24~30

7~13

25~30

30~35

25~30

Original Sheet Size
(cm)

100*200

100*200

100*200

100*200

100*200

100*200

Original Sheet Thickness
(mm)

80

80

80

36

32

38

Tensile Strength
(kg/cm^2)

2.0

3.2

2.8

9.5

11.8

9.5

Elongation at Break (%)

180

180

340

220

160

120

Tear Strength (kg/cm)

1.9

2.4

2.1

3.4

3.8

3.3

Compressive Strength
at 25% Deflection
(kg/cm^2)

0.4

0.6

0.3

0.7

0.8

0.7

Compressive Strength
at 50% Deflection
(kg/cm^2)

1.0

1.3

0.8

1.5

1.8

1.6

Compression Set
to 50% of
Original Thickness
(%)

10

14

17

20

20

20

Water Absorption
(%, by weight,
room temp., 5 hrs)

< 1

< 1

< 1

< 1

< 1

< 1

Type

PE/EVA

PE/EVA

EVA/PE

EVA/PE

EVA/PE

EVA

Item No.

A-35

RE-1050

B-20HV

P-560

P-565

Density
(g/cm^3)

0.075~0.085

0.075~0.085

0.11~0.115

0.125~0.135

0.17~0.18

Hardness
(type C)

32~38

45~50

20~25

55~60

60~65

Original Sheet Size
(cm)

100*200

94*188
100*200

100*200

90*180
110*235

100*190
100*220

Original Sheet Thickness
(mm)

24

32
40

43

32
32

28
28

Tensile Strength
(kg/cm^2)

9.4

13.0

9.3

18.8

26.4

Elongation at Break (%)

90

130

140

120

150

Tear Strength (kg/cm)

3.2

3.3

2.8

5.6

8.3

Compressive Strength
at 25% Deflection
(kg/cm^2)

0.8

0.9

0.5

0.8

1.4

Compressive Strength
at 50% Deflection
(kg/cm^2)

1.5

1.5

1.2

1.3

2.4

Compression Set
to 50% of
Original Thickness
(%)

10

30

20

2

1

Water Absorption
(%, by weight,
room temp., 5 hrs)

< 1

< 1

< 1

< 1

< 1

Type

PE/EVA

PE/EVA

EVA

EVA/PE

EVA/PE

examination project 

unit

name

L-1500

L-2000

L-2500

L-3000

L-4000

tensile strength at break

mpa

0.25-0.3

elongation at break

%

240-290

220-250

180-230

170-200

150-180

ASKER“ C” hardness

°

40-45°

30-35°

20-25°

15-20°

12-15°

tear strength

KN/M

7-10

8.5-11

9-12

density

Kg/m 3

60Kg/m 3

50Kg/m 3

40Kg/m 3

30Kg/m 3

25Kg/m 3

compression set

%

54.2

compression set

Ø 23mm        specimen

%

0.2
percent of pass94%

0.2
percent of pass94%

0.2
percent of pass94%

0.2
percent of pass94%

0.2
percent of pass94%

24h*25%

50*50mm  specimen

%

combustion test(straight)

B1

32

32

32

B2

26

26

26

ignitability

≤ 150