JCG Dia:20-150mm Forged Grinding Steel Ball

Name

Material

C

Mn

Si

Cr

S

P

JC-1

50Mn

0.48-0.56

0.70-1.0

0.17-0.37

≤0.25

≤0.035

≤0.035

JC-2

60Mn

0.57-0.65

0.70-1.0

0.17-0.37

≤0.25

≤0.035

≤0.035

JC-3

65Mn

0.60-0.70

0.90-1.2

0.17-0.37

≤0.25

≤0.035

≤0.035

JC-4

B2

0.70-0.85

0.70-0.80

0.17-0.37

0.2-0.7

≤0.03

≤0.03

JC-5

75SiMn

0.70-0.90

0.70-1.20

0.4-0.8

≤0.25

≤0.03

≤0.03

JC-6

Wear-resistant Alloy

0.50-0.65

0.4-1.0

1.4-1.8

0.9-1.2

≤0.03

≤0.03

 Name

Material

Impact Test(Ak.J/cm²)

Endurance Test Times(5m/T)

Surface Hardness

(Φ25mm- Φ60mm)

Core Hardness

(Φ25mm- Φ60mm)

Surface Hardness

(Φ70mm- Φ100mm)

Core Hardness

(Φ70mm- Φ100mm)

Breakage

JC-1

50Mn

≥12

≥10000

≥56

≥35

≥56

≥28

<1%

JC-2

60Mn

≥13

≥10000

≥58

≥38

≥58

≥29

<1%

JC-3

65Mn

≥15

≥12000

≥60

≥42

≥60

≥30

<1%

JC-4

B2

≥17

≥12000

≥60

≥52

≥60

≥50

<1%

JC-5

75SiMn

≥16

≥12000

≥60

≥50

≥60

≥48

<1%

JC-6

Wear-resistant Alloy

≥17

≥12000

≥60

≥54

≥60

≥52

<1%

 Norminal Diameter

Diametrical Tolerance(mm)

Approx Weight of Single Ball(kg)

Average Number of One MT

Microstructure

25mm/1''

+1.5,-0.5

0.064

15625

M+B+C

(M-Martensite;B-Bainitic;C-Carbide)

30mm/1.25''

+1.5,-0.5

0.11

9090

40mm/1.5''

+2.0,-1.0

0.26

3846

50mm/2''

+2.0,-1.0

0.51

1961

60mm/2.5''

+3.0,-2.0

0.89

1124

70mm/2.75''

+3.0,-2.0

1.4

714

80mm/3.25''

+3.0,-2.0

2.1

476

90mm/3.5''

+3.0,-2.0

3

333

100mm/4''

+4.0,-3.0

4.1

244

110mm/4.5''

+4.0,-3.0

5.47

283

120mm/4.75

+4.0,-3.0

7.1

141

130mm/5''

+4.0,-3.0

9.02

111