Rigid Foam Polyurethane for Continue Sandwish Panels

Specifications

DBC-402A panels uses special blend polyether polyols as the main raw materials with special additives to constiture blend polyols, the characteristics are as follows,

1.good flowability in the reactivity process, the foam density distributes uniformity, with excellent dimensional stability and cohesiveness.

et different requirements of continuous sandwich board product lines

Physical Properties

Appearance                       pale yellow transparent viscous liquid

Hydroxyl Value mgKOH/g                            300-400 

Dynamic Viscosity (25 °C) mPa.s             150-300

Gravity (20 °C ) g/ml                                    1.10-1.16

Storage Temperature °C                             10-25

Storage Stability month                                   6

Recommended Ratio                                  pbw 
DJD-103 blend polyols                                100

Isocyanate                                                  100-110

Technology and Reactivity  (the exact value varied depending on processing conditions)

                                                                 Manual Mixing          Mechanical Foaming 

Raw material Temperature °C                   25                                  25

Mold Temperature °C                                40-45                              40-45

Rise time s                                                 10-20                              6-15

Gel time s                                                    35-65                              20-40   

Free Density kg/m3                                   30-35                              30-35

Foam Performance

Foam Density by Molding                              GB/T 6343          ≥ 40kg/m3

Closed-cell Rate                                            GB/T 10799        ≥90%

Thermal Conductivity (15 °C)                       GB/T 3399          ≤22 mW/(m.K)

Compressive strength                                   GB/T 8813          ≥100kPa

(perpendicular to the direction of rising)            

Dimensional Stability                                    GB/T 8811      

(24h, -20 °C)                                                                                  ≤1.0% 

(24h, 100 °C)                                                                                 ≤1.5%

Flame retardant grade                                   GB/T 8624           Level  B2