High Temperature Anticorrosive Epoxy Vinyl Ester Resin

Specifications

TH-110 is a medium-viscosity, non-prepromoted bisphenol-A epoxy vinyl ester resin modified by methyl acrylic acid,it has excellent resistance to chemical corrosion, good mechanical properties, low shrinkage, good operational characteristics,it has been applied in a wide range of end-use FRP applications and fabricator techniques, especially it can provide resistance to a wide range of organic and inorganic acids, alkalis, salt solution, oxidizing chemicals, bleaches and organic solvents for use in many chemical industry fields. it is an ideal harsh anti-corrosive glass fiber reinforced plastic resin

Advantages

• Excellent resistance to acids, alkalis, salt and organic solvent, reach the anti-corrosive level of Derakane Momentum^TM 411-350 and RIPOXY R-802;
• Good mechanic properties, high tensile elongation, good toughness;
• Good glass fiber invasive and good fabrication operability;
• HDT of pure resin casting up more than 120°C.

Application

• Corrosion-resistant FRP lining and the overall FRP storage tanks, pipelines, towers, tanks and other chemical equipments and products;
• Pultrusion FRP products, grid and electrical insulation FRP materials;
• Available for HLU, FW, PL, SPU, RTM, flake glass, filled linings and coating compounds.

Typical Liquid Resin Properties

¹Typical properties; not to be construed as specification;

² Promoter: Nap-Co(cobalt napthenate) or Is-Co(cobalt iso-octoate),Co content:6%; curing agent: MEKP (methylethylketone peroxide) , effective oxygen content:10%;
³ No additives,promoters, accelerators, sealed, dark and shade. Shelf life is quality guaranteed, not the storage period of time, the storage time is far exceeds guaranteed of shelf life.

Typical Room-Temperature Properties⁽¹⁾ of Postcured⁽²⁾ 4mm Resin Castings

¹Typical properties; not to be construed as specification; values reported by GB standards
² Cure schedule: 24 hours at room temperature; then 2 hours at 120°C(250°F)

Typical Room-temperature Properties⁽¹⁾ of Postcured⁽²⁾ 6mm Laminate⁽³⁾

¹Typical properties; not to be construed as specification; values reported by GB standards

² Cure schedule: 24 hours at room temperature; then 2 hours at 120°C(250°F)

³ 4mm laminate construction: HLU, S/M/M/M/S, S= continuous veil glass, 30g/m²; M=chopped strand mat, 450g/m²

Recommended Ratio (Wt%)

Remark:Users need to adjust the amount of “blue water” (Nap-Co or Iso-Co accelerator) and “white water” (MEKP curing agent) and their ratio for the right gel time according to the actual temperature. Different cobalt content of the accelerator and the effective oxygen content of the curing agent have the different curing effects, users must take the actual small test to confirm the amount of “blue and white water”. If high humidity or low temperature, the curing system by adding an appropriate amount of DMA (dimethylaniline), or the curing system by using BPO (benzoyl peroxide)&DMA are the better choice. Such as heat release of resin, gel time, “blue and white water” has special demands, please no hesitate to contact Tianhe Co.

Resin corrosion resistance
 As the corrosive mediums are too much, the detailed anti-corrosive guide data are not provided, if necessary, please contact us to demand anti-corrosion data sheet to determine how the selection or take on-site etching method with help of us.

Package&Storage and Safety Information

Package:200kg or 18kg clean and dry iron drum;

Safety suggestion:Accelerator and curing agent must be separated during the storage and transportation;

Skin and eyes should be avoided to contact with resin, and necessary protective equipment and clothing should be

worn, prohibit strictly pour into the water. For details, please see the MSDS.

Storage&Transportation: Drums-store at temperatures below 25°C/77°F, Storage life decreases with increasing storage temperature, Keep away from flames, fire and sparks, and no smoking, avoid exposure to heat sources such as direct sunlight or steam pipes, Store separately from oxidizing materials, peroxides and metal salts,Keep container closed tightly when not in use, don’t store outdoors, and avoid contamination of product with water. Should be refrigerated truck transport from May to October, at least at night, any inappropriate storage and transportation will lead to reduced resin shelf life; remove the drum top to replace the air and agitate in a period of time can extended the resin shelf life.

Particular remark:this technical data sheet and any information are our company 2008 version,they may be adjusted as technology development, we reserves the interpretation and amendment right without any Advance notice.