Prime Hot Rolled Low Carbon Mild Wire Rod Steel Sae1006-sae1018, 5.5-16mm

Type

SAE1008 /SAE1006/Q235/A3 hot rolled alloy low carbon steel wire rods

technique standard

SAE1006,SAE1006B,SAE1008,SAE1008B,Q235,A3,42CrMo,30Cr

Grade

SAE1006,SAE1006B,SAE1008,SAE1008B,Q235,A3,42CrMo,30Cr, SWRH72B, SWRH82B

Size

5.5mm,6.5mm,8mm,10mm,7mm,9mm,11mm,12mm,14mm

Application

drawing blank ,building materials, machinery parts, construction

civil engineering construction,like Housing, Bridges, roads.

Delivery state

Hot rolling forming,Normalizing,hot rolled state

Packing

Export standard packing

Coil weight

1.8-2.1mt

Delivery

25days when get the down payment or workable L/C.

Payment

T/T or LC at sight

Grade

Chemical Composition(%)

C

Mn

Si

S

P

B

SAE1006B

0.03~O.07

≤0.32

≤0.30

≤0.045

≤0.040

>0.0008

Mechanical properties

Yield strength(N/mm²)

Tensile strength(N/mm²)

Elongation(%)

250-280

350-380

≥32

Grade

Chemical Composition(%)

C

Mn

Si

S

P

B

SAE1008B

0.10max

0.3~O.50

0.15max

0.050max

0.040 max

0.0008 min

Mechanical properties

Yield strength(N/mm²)

Tensile strength(N/mm²)

Elongation(%)

≥195

315-430

≥30

Grade

Chemical Composition(%)

C

Mn

Si

S

P

B

Q195B

0.06~O.12

0.25~O.50

≤0.30

≤0.050

≤0.045

>0.0008

Mechanical properties

Yield strength(N/mm2)

Tensile strength(N/mm2)

Elongation(%)

≥195

315-430

≥33

Grade

Chemical Composition(%)

C

Mn

Si

S

P

B

Q235B

0.12~O.2

0.3~O.701

≤0.30

≤0.045

≤0.045

>0.0008

Mechanical properties

Yield strength(N/mm2)

Tensile strength(N/mm2)

Elongation(%)

235

375-500

≥26