silver brazing flux paste used for hard alloy and diamond Saw blade suitable for furnace brazing and flame brazing

 Silver Solder Flux Paste QJ102

HZ-QJ305 can work together with silverbased brazing alloysfor copper and copper alloys, stainless steel, nickel alloys, diamond PCD at the temperature range of 600 to 850 °C in flame brazing, resistance welding, highfrequencybrazing, furnace brazing.

Physical status: 

paste  Granularity:≤150μm   Density: 1.9-2.1   Standard: JB/T6045-92

Chemical composition: 

complex borate, complex fluoborate, activities, water etc. No contain restricted compounds.

Characters: 

The flux is very stable chemically and physically. No precipitate, caking or loss of activity and fluidity for long time storage. Featuring smooth surface and small welding seam, HZ-QJ305 can replace similar foreign product. 

Application areas:

 Refrigerator accessories, compressor, stone and wood cutter, automobile accessories, glass frame, ornament and jewelry, electric apparatus, hardware tools, etc.

Preparation:

To optimize the result, the work pieces should be cleansed thoroughly previous to brazing operation, the surface should not be too rough or attached on metallic particle or dirt. Stainless steel work piece should not be scrubbed by steel wire brush.

Operation: 

Dip the work pieces into the paste or diluted paste before brazing.

Post treatment:

The residue can be eliminated by merging the work piece into hot water on 10% mass fraction citric acid.

Caution: inesculent. Immediate water flashing is need if it is splashed into eye or mouth. Do not mix it with otherimpurity materials. After the packing is opened, the paste can be hardened easily. 

Related product: