SILVER SOLDER RODS MANUFACTURING

Nominal composition (weight %):HZ-Ag35C

Ag: 35

Cu: 26

Zn: 21

Cd: 18

Physical characteristics

Melting range (Solidus – Liquidus): 607 – 702 °C

Brazing temperature: 645 °C

Density: 8,7 g/cm3

Tensile Strength: 42 kg / mm2

Range of application:

HZ-Ag35C is a cadmium-bearing silver brazing alloy, with high melting point and wide melting range.It can be used to join ferrous, non ferrous and dissimilar metals and alloys, such as steel, copper, copper Alloys. Due to its wide melting range, it can be used with good results when joint clearances are large and/or not uniform. With this alloy particular care must be taken to keep brazing cycles as short as possible, in order to avoid possible Zinc volatilization, which will result in porosity and/or voids in the joint fillet. When Zinc volatilization is a concern, a special version of this alloy, HZ-Ag35C, with little additions of Silicon (approx. 0,2%) is recommended to be used. When brazing in an oxidizing environment a proper flux should be used. Due to the content of Cadmium special safety precautions must be followed during brazing operations (e.g., avoid of overheating, use of mechanical ventilation, wear of respiratory masks).

Characteristics Make-up:

Rods: Ø 0.5-4.0 mm Length: 400- 1.000 mm

Wires: Ø 0.3-3.5 mm (spooled and coiled)

Strips: Thickness: 0.1-1 mm Width: 1.5-105 mm

Rings

Preforms from Wire and from Strip

Pastes & Powders

Other dimensions are available upon request