Aluminum Base Aluminum Brazing Rods Filler Rod

Specifications

Aluminum welding rod: 
1. low melting temperature. 
2.good fluidity 
3. little deformation for parent material 

As one of the most common aluminum welding materials,  Aluminum welding rod 4047 are often used for soldering and brazing of casting aluminum, and extrusion molding of aluminum and aluminum alloys with aluminum welding flux.

Advantage:          

1. low melting temperature.

2.good  fluidity

3. little deformation for parent material

Standard: GB/T 10858-2008

Physical Property:

Yield Strength Rp0.2(Mpa): 40

Tensile Strength: above 130

Density: 2.66kg/dm3

Melting Range:573-632°C

Processing Temp.:600-645°C

Chemical Composition (%):

Al:Remain Si:4.0-4.5 Cu:0.3 Mg:0.05 Zn:0.1 Other:<0.5

Parent Metals: AlMgSi(6000 series) alloys. E.g. 6063,6082 cast alloys of aluminum-silicon type. Not recommended for welding AlMg alloys

Welding Process:MIG or TIG

Anodizing: Poor

Corrosion Resistance: Good but can depend on parent alloy

Our aluminum wire, sheet and rod are manufactured to the highest quality standards and undergo unique testing methods in order to ensure maximum feedability and weld quality.

Our Huazhong Aluminum Brazing alloy is your best choice to achieve the best possible welds: every time, every spool.