REOO China EVA FILM for manufacturing solar panel

Whole Set Solar Panel Manufacturing Equipment with Raw

Materials

JCC  EVA Solar cell encapsulation film model:
Fast Cure:JCC-105; High penetration type:JCC-105 -T

product specification :
1,Lamp shape:EVA Ultra Barrier Solar Films are Double stripe type;and also
can manufacture products of other stripes according to customers’ needs.
2,Product thickness:We can supply different thickness arranging from
0.30-0.80mm, the thickness of conventional product are 0.40mm and 0.50mm,
thickness tolerance:±0.03mm.
3,Product width: any width below 2000mm, and the normal width: 350,550,
680,810,820,980,1000mm, width tolerance: ±3mm
4,Length of each roll:100m,Tolerance:±1 m can manufacture according
to customers’ needs

Curing process conditions:
JCC-105/ JCC-105-T Suggested laminating temperature:140±2℃(can
change according to customers’ needs)
pumpdown time 4-6min
Laminated time 8-10min

Technological conditions :
To ensure the quality of modular package, we suggest that after the
calibration of laminating machine temperature, following the technological
conditions can ensure EVA film crosslinking degree is above 80% and then
ensure the quality.If you want to increase the degree of crosslinking layer , you can
be appropriately raise the temperature or pressure holding time
1, JCC-105/JCC-105-T:
Laminating machine temperature 138-142℃,vacuumize 5min,forcing
60s,Laminated keep 8-10min.
2,Laminating instructions:
(a),Laminating conditions according to the performance of the laminating
machine. According to the temperature characteristics of each
laminating machine,tracking test must at any time,Selection of

crosslinking degree between 70% ~ 70% after curing of process
conditions is preferred.Crosslinking degree is too low or too high can
lead to poor late aging performance.
(b),If laminating machine working environment temperature is different,
process conditions should be adjusted, specific to each laminating
machine parameters shall prevail.
3, After the completion of the laminated,Should after the temperature of
laminated good components down natural 80 ℃ and then Then open
the warm cloth , remove the components to trimming and deflashing .

Contact informatioin

                    

   

Mr.Simon Sun   NANTONG REOO TECHNOLOGY CO.,LTD.   Add: Chennan industrial park, Rudong, Jiangsu, Chima   PC226400   Tel: 86 513 8410 5399   Fax: 86 513 8410 5505   Skype: reoolisa   WhatsApp: 0086 188 629 38063