optical glass borosilicate glass raw borosilicate glass

Specifications

3.3 Borosilicate float glass

3.3 Borosilicate float glass is produced by the technology of float glass making .Main ingredients of this float glass are sodium oxide(Na2o),boron oxide(B2O3),silicon dioside(si02).In those ingredients ,boron and silicon have high content .For example , boron :12.5~13.5%,silicon 78~80%.In this case , this special glass are called borosilicate float glass. The feature of the glass is that it has small thermal expansion coefficient ,good thermal stability, chemical durability and electrical property. Therefore ,borosilicate float glass chemical resistant ,heat resistant and mechanical property are excellent .Moreover, the glass could use in high temperature and has strong hardness .So, borosilicate glass is called heat resistant glass as well. It is a special flameproof glass.

Product Performace:

1. Mechanical property 

Density (ρ):2.23±0.03g/cm3

Mohs’hardness:>7

2. Thermodynamic property

 Thermal expansion coefficient:

(0-300°C)(3.3±0.1)x10-6K-1

Intenerate temperature :820±10°C

Strain temperature: 516±10°C

Specific heat capacity: (20-100°C)0.82KJ x( x K)-1

Thermal conductivity coefficient:1.2W x(m x K)-1

Heat resistant :180 K 

(Become tempered glass ,300K above)

With piece temperature difference performance :100K 

(Become tempered glass,200K above)

A long –term (>10h) temperature loading capacity of 450 °C,a short-term (<10h)temperature loading capacity of 500 °C.

3.Chemical property 

  Water resisting property:

 ISO719/DIN 12111 HGB1

 ISO720           HGA1

Acid proof :ISO1776/DIN121161

Alkali resistance :ISO695/DIN52322 A2

4.Optical performance 

Index of refraction :Nd:1.47384

5.Electric property

Electric receptivity (lgρ):50 °C 8.0 W x

Dielectric loss:

Tan s (1 mhz 20°C)38x10-4

Specific inductive capacity (SIC) e:4.7

6.Maxmium size :850mm x2000mm

7.Thickness :2~12mm

Applications

·Home application (e.g. internal panels in ovens and panels in microwave oven ,induction heater ,fireplace ,space heating appliances etc.)

·Environmental project and Chemical project(e.g. underlayer of repellency)

·Lighting industry (e.g. cover panels for high power floodlights and projectors)

·Solar electrical energy generation (e.g. top of solar battery)

·Accuracy apparatus (e.g. optically flat filter)

·Semiconductor technology (e.g.water)

·Medical Technology biological engineering

·Protection (e.g. bullet –resisting glass ,cover of high grade watch

·Advance building flameproof glass