2205 dual-phase steel black bar

PRODUCT SHOW:

1. Pictures of    2205 black bar

 2.Product Features of    2205 black bar

Product feature

DDuplex stainless steel 2205 alloy is consisting of 22% chromium, 2.5% molybdenum and 4.5% nickel nitrogen alloy. It has high strength, good impact toughness, good overall and local anti stress corrosion..

the yield strength of the 2250 duplex stainless steel is two times that of the austenitic stainless steel. This feature makes the designer lose weight when designing the product, and make this alloy more price than 316317L. This alloy is especially suitable for the temperature range of -50 F and F/+600.. The application of the temperature range beyond the range of the temperature can also be considered, but there are some limitations, especially for welding structure.

Application 

- pressure vessels, high pressure storage tanks, high pressure piping, heat exchangers (chemical processing industry).

- oil and gas pipelines, heat exchanger tubes.

Sewage treatment system.

- the pulp and paper industry classifier, bleaching equipment, storage and processing system.

- high strength and corrosion resistant environment of the rotary shaft, press roll, blade, impeller, etc.. 

-A cargo box for ships or trucks

- food processing equipment

Corrosion resistance

Uniform corrosion

Because of Cr content (22%), molybdenum (3%) and nitrogen content (0.18%), the corrosion resistance of 2205 is better than 316L and 317L in most environments.

Local corrosion resistance

2205 the contents of Cr, Mo and nitrogen in duplex stainless steel make them in oxidizing and acidic solution, and have strong resistance to pitting corrosion and crevice corrosion..

Stress corrosion

Dual phase microstructure of stainless steel is helpful to improve the resistance of the stainless steel stress corrosion cracking ability. In the case of certain temperature, tension, oxygen and chloride, the austenitic stainless steel will have the stress corrosion of the chloride. Since these conditions are not easy to control, the use of 317L, 316L and 304L is limited in this respect.

Corrosion fatigue

2205 the high strength and corrosion resistance of the dual phase steel have high corrosion fatigue strength. The machining equipment is easily influenced by corrosion environment and load cycle, and the characteristic of 2205 is suitable for this application.

3.Chemical composition:  

C :≤0.03,Si :≤1.00,Mn :≤2.00,P :≤0.04,S :≤0.030,Ni :4.5-6.5,Cr :21.0-24.0  

N:0.08-0.20 ,Mo:2.5-3.5

4.Production Flow of   2205 black bar