AZS RAMMING MASS

Product Description

THIS MATERIAL IS WITHOUT PHOSPHORUS,

AND DOES NOT POLLUTE THE ENVIROMENT.

USAGE: 1. Open the bag to check if the coagulant agent is dampened or hardened, and then spread the coagulant agent uniformly into the bag;

Mix certain amount of the mass according to on-site assumption. When it mixes well, add room temperature water by a ratio of 6-7%, or adjust the ratio according to local climatic condition and water content of the mixture. Blend it till there is no raw ramming mass left or till that it will break into pieces instantly when it falls to the ground after one unlooses his grip of the mass from the height of 0.33 meters;
The construction site and bonder should be clean and without sundries. The leftover well-mixed mass should be covered with plastic sheet film or placed in shady and cool place. The mass that is not dry and hard can be used again; otherwise, it should be crushed and used together with other raw material or abandoned.
Mix with water to make the material likeslurry then press smooth by vibrating.

CONCRETING TIME: BEGINNING TIME: 0:15~2:00 HOURS

FINISHING TIME: 3:00~6:00 HOURS

HEATING TIME: AFTER 150:00 HOURS

$Refractoies Azs Ramming Mass$

Physical and chemical index

Item		Behaviors
Item		AZSR-50V	AZSM-06J	AZSM-05	AZSM-04L
Chemical Composition%	Al₂O₃	48	48	48	48
	ZrO₂	30	30	30	30
	SiO₂	20	20	20	20
	Others	2	2	2	2
Bulk density g/cm3		3.2	3.1	3.1	3.1
Crystallographic analysis after being sintered at 1300/1500°C		Corundum, zirconium oxide	Corundum, zirconium oxide	Corundum, zirconium oxide	Corundum, zirconium oxide
Thermal conductivity		Good	Good	Good	Good
Anti-corrosion property		Excellent at 1300°C	Excellent at 1300°C	Excellent at 1300°C	Excellent at 1300°C
particle diameter of grain		0-5mm	0-0.6mm	0-0.5mm	0-0.4mm
Application temperature		Cold/low temperature	Cold/low temperature	Cold/low temperature	Cold/low temperature
Quantity of water		8-10% (proportion by weight)	10-12% (proportion by weight)	10-12% (proportion by weight)	10-12% (proportion by weight)
Solidification		Water (ceramic)	Water (ceramic)	Water (ceramic)	Water (ceramic)
Packaging		25kg/bag	25kg/bag	25kg/bag	25kg/bag
Quality guarantee period		12 months	12 months	12 months	12 months
Used for		Under bottom paving, spreading, Melting end and working area	Under bottom paving, spreading and the place between fused cast brick and ERSOL 50	Under bottom paving, spreading, and the joint between bricks of two layers that are between the fused cast brick and ERSOL 50	Joint between bricks of two layers

$Refractoies Azs Ramming Mass$ $Refractoies Azs Ramming Mass$

Zhengzhou Sunrise Refractory Co., Ltd.: Contact nameAmy Wang
Chat Now; Phone86-371-63838939; AddressNO 36 Fengchan Road zhengzhou Henan China, Zhengzhou, Henan

Cement Industry	Ceramic Fibre	Chrome and Corundum brick	Electrocast Zirconia
Fireclay and Alumina brick	Fused Cast Alumina	Fused Cast AZS	Glass Mold Brick
Insulation Bricks	Magnesia Brick	Metallurgy industry	Mullite and Sillimanite brick
New Products	Silica brick	Zircon Brick