AISI O1/ DIN1.2510 Steel Round Bar/Steel 1.2510 Material

1.Specification of Steel 1.2510 Material

       Round bar 

Diameter(mm)

Length (mm)

20~70

2000~5800

         Plate

Thickness(mm)  

Width (mm)       

Length (mm)    

20~70

105~610

2000~5800

The specification can be customised!

2.Chemical compositon of Steel 1.2510 Material

NO.

C

Mn

Si

Cr

W

V

P

S

Steel 1.2510 Material

0.85~1.00

1.00~1.40

0.10~0.50

0.40~0.60

0.40~0.60

≤0.030

≤0.030

≤0.030

3.Delivery condition 

Standard Number

   Annealing 

   Quenching 

Cold drawn

Steel 1.2510 Material

≤255

≤269

4.Heat treatment 

Isothermal annealing:

-Heat to 870÷880°C;

-Furnace cooling to 760°Cand hold at temperature for at least 10 hours;

-Cool by 10°C/h to 720°C;

-Cooling in air.

Stress relieving:

To be carried out after machining and before the final heat treatment.

-Heat to 650-700°C, hold for 4/6 hours:

-Furnace cooling to 330-350°C;

-Cooling in air.

Hardening:

-Initial preheating to 350-450°C;

-Second preheating to 750-850°C

- Austenitizing at 1010-1040°Cor at 1080-1100°C;

-Cooling in air or in oil if large parts.

Tempring hardness: 62-66 HRC

Tempering:

    In the temperature range 150-300°Cwith minimum holding time 3 h. For parts hardened 

at 1080-1100°C, a first tempering will be carried out at 500-550°Cin order to exploit secon

dary hardness, followed by a second tempering at 180/300°C.

5.Characteristic of Steel 1.2510 Material

(1)Good quenching resistance, heat deformation small, wear-resistant, impact resistant.

(2)Vacuum degassing refining processing pure steel.

(3)Spheroidizing softening process, good cutting performance.

(4)Strengthen the elements vanadium, molybdenum special join, 

is extremely excellent in wear resistance.

6.Application of Steel 1.2510 Material   

(1)Thickness of not more than 2MM sheet, efficient blanking die, punch die and pressure die etc.

(2)All kinds of scissors, inserts, woodworking blade.

(3)Thread rolling die and wear-resistant slider.

(4)Cold Heading Die, thermosetting resin molding.

(5)Molding in deep drawing cold extrusion dies.

(6)For pounch mold,knife mold,screw mold,chinaware mold.

Hot work tool steel

DIN

1.2344,1.2343,1.2365,1.2581,1.2367,1.2713 etc.

AISI

H13,H11,H10,H21, etc.

JIS

SKD61,SKD6,SKD5,SKT4 etc.

Cold work tool steel

DIN

1.2601,1.2379,1.2080,1.2363,1.2842,1.2419,1.2510,1.2550,1.2767 etc.

AISI

D2,D3,D5,D6,D8,A2,O2,O1 etc.

JIS

SKD1,SKD11, SKS3 etc.

Plastic mould steel

DIN

1.2083,1.2311, 1.2316,1.2738 etc.

AISI

P20, P20+Ni, 420 etc.

JIS

NAK80

High speed tool steel

DIN

1.3355,1.3343

AISI

T1,M2,M35,M42

JIS

SKH2,SKH51

Structural alloy steel

DIN

1.7225,1.6511,1.7035,1.7220

AISI

4,140,434,051,404,130

JIS

SCM440