chemical composition of 42crmo4

Preheat the steel carefully, then raise the temperature to 1150-1200°C for forging. Do not forge below 850°C.

Heat the AISI 4140 slowly to 800-850°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 480°C followed by air cooling.

When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening. 

AISI 4140 steel is usually supplied ready heat treated to 18-22HRC. If further heat treatment is required annealed AISI 4140 should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.

Heat the AISI 4140 carefully to a suitable temperature selected by reference to a tempering chart or table (usually between 550-700°C, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air. Tempering between 250-375°C is not advised as tempering within this range will seriously reduce the impact value.

(*at room temperature heat treated to 18-22HRc)

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each AISI 4140 steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of alloy steel.

Lara Liao

Tel:        +86-0769-3389 9333

Fax:       +86-0769-8870 5839

Skype:    lara.liao80

Email:      laraliao AT toolsteel DOT net DOT cn

               lara AT otaisteel DOT com

TM:        cn1511348531

Mobile:   86 3711884714