Magnesite Fire-resistant Board Production Line

Specifications

Magnesite Fire-resistant Board Production Line

 I.Usage and Technical Index of Product

The Magnesium Oxide Board (Glass Magnesium Board or MgO Board)is made of filling materials, such as sawdust and all kinds of crushed plant straw (you can select any one kind ) and several chemical raw materials which are token as modified material after special technology. The board has such features: quickly hard, high strength, large format, fireproofing, dampproof and good waterproof performance. It can be nailed, planed and sticked, so it can be used widely at indoor decoration, such as wall skirting and ceiling of market, hotel, club, station, office building and living room. And it can get large usage at topgrade furniture, door and partition. This product is made of waste materials, and it is ideal product which can replace all kinds of wood broad with reasonable price and good quality.

Technical index:

1. Oxygenic index%: 90

2. Level combustion: SO

3. Vertical combustion: SO

4. Water content rate: 10.9%

5. Capacity: 1.15g/cm3

6. Static bending intensity: 169.46Mpa

7. Density: T/ m3 1.13

8. Water resistance: Without chalking for 24 hours and there is no change on surface

9. No “Three-wastes” (waste water, waste gas and waste residue), no pollution and environmental protection         

 (I) Cost accounting

Raw material cost: 15 Yuan/ Piece; Wage: 0.5Yuan/ Piece;  Water-electricity fee: 0.2 Yuan/ Piece; Depreciation of the workshop: 0.2Yuan/ Piece; Total: 15.90 Yuan/ Piece

 (II) Profit analysis: production: (Take the middle-scale equipment as example),400 pieces per day, at the common price of 40 Yuan/ Piece to sell, and then the profit per piece is that: 40 Yuan/ Piece-15.9 Yuan/ Piece=24.1 Yuan/ Piece, the profit per day is that: 400 pieces×24.1 Yuan/ Piece=9640Yuan